Ethylene Vinyl ′ Acetate Copolymer Va 18% 28% Granules EVA Resin

• Carrier: EVA
• Color: White
• Grade: Hot Melt Grade Injection Grade
• Characteristic: High Transparency
• Material: Ethylene-Vinyl Acetatecopolymers/EVA
• Usage: General Plastics, Engineering Plastics, Specialty
• Form: Granule
• Mfr: 0.6 - 0.8 G/10 Min
• Plastic Properties After Heated: Thermoplastic Plastics
• Transport Package: 25kg/Bags
• Specification: Va28% Va19% Va 18%
• Origin: China
• HS Code: 3901909000
• Production Capacity: 4000000/Mt

Product Description

 

Product Description

Product Description

 

Product Name : 18% 19% 28% VA Prime EVA Resin Raw Material

Product Feature :

EVA resin is an ethylene-vinyl acetate copolymer, with a general vinyl acetate (VA) content of 5% to 40%. Compared with polyethylene and EVA, due to the introduction of vinyl acetate monomer into the molecular chain, the high crystallinity is reduced, the flexibility, impact resistance, filler compatibility and heat sealing performance are improved, and it is widely used in foam shoes Materials, functional sheds and other films, packaging films, hot melt adhesives, wires and cables, toys and other fields.

EVA is a high fluidity, high VA content ethylene vinyl acetate copolymer (EVA), which has many excellent properties, such as unique flexibility and elasticity, thermal stability, good low temperature resistance, good compatibility sex and non-toxic etc.

EVA Ethylene-vinyl acetate Pellet is a thermoplastic polymer formed by the copolymerization of ethylene and vinyl acetate.
It is a flexible, lightweight material that can be easily machined into various shapes.
EVA resin has good impact strength and is widely used.

 

Detailed Photos

 

Product Parameters

  EVA16%

PROPERTIES	TEST METHOD	UNIT	Data
VA Content		%	16.0
Density	ASTM D1505	g/cm3	0.937
Melt Index MI2.16	ASTM D1238	g/10min	1.5
Tensile Strength (Break)	ASTM D638	Kg/cm2	170
Elongation at break	ASTM D638	%	700
Melting point	ASTM D-3418	ºC	89
Hardness	ASTM D2240	Shore D	37

EVA 18%

Properties	Test method	Value
VA Content(%)	USI	18
Density(g/cm3)	ASTM D792	0.939
Melt Index (g/10min)	ASTM D1238	2.5
Tensile Strength(Molded)(Break)(kg/cm2)	ASTM D638	180
Ultimate elongation(Molded)(%)	ASTM D638	750
Low Temperature Brittleness(ºC/F50)	ASTM D746	<-76
Vicat Softening Point(ºC)	ASTM D1525	64
Melt Point (ºC)	ASTM D3418	86
Hardness(Shore D)	ASTM D2240	36

EVA28%

PROPERTIES	TEST METHOD	UNIT	Data
VA Content		%	28.0
Density	ASTM D1505	g/cm3	0.954
Melt Index MI2.16	ASTM D1238	g/10min	15
Tensile Strength (Break)	ASTM D638	Kg/cm2	80
Elongation at break	ASTM D638	%	>800
Melting point	ASTM D-3418	ºC	69
Hardness	ASTM D2240	Shore D	20

Application

 

Mainly used in shoes, slippers, toys production 

 

Packaging & Shipping

 

25kg/ carton or 25kg/bag, or per your requirement

25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container

product display